Toshiharu Enomae, Fumihiko Onabe and Makoto Usuda
The absorption
rate of organic liquids and ethanol aqueous solution into wood free paper or
coated paper was measured using Bristow's method, though water and oil
absorption has been studied by many researchers.
As for organic
liquids, liquid transferring rate was found to follow Lucas-Washburn's equation
and all measured points were almost plotted on the same line in the figure.
However, a minute difference shown was considered to result from the extent to
which the respective organic liquids swelled cellulose. When ethanol aqueous
solution was absorbed, transferred liquid volume increased gradually even for
the initial wetting time which originally meant the time when it kept constant.
And the increase rate became larger with ethanol concentration. As for
absorption of water or ethanol aqueous solution into slack sized wood free paper,
liquid transferring rate was observed to be almost proportional to the contact
time. Consequently, Bristow's equation could not apply. Swelling and water
molecular
The roughness
index Kr calculated from the line of organic liquids by Bristow's method corresponded
to Bekk smoothness as for uncoated paper. However, its comparison between
coated and uncoated paper was not reasonable, possibly because of the
difference in the chemical property and compressibility of the paper surface.
紙パ技協誌44(7):811-820(1990).
--------------------------------------------------------------------------------
紙の液体浸透特性について（第１報）
－有機液体及びエタノール水溶液の浸透－
--------------------------------------------------------------------------------
東京大学農学部
江前敏晴・尾鍋史彦・臼田誠人
--------------------------------------------------------------------------------
要旨
アニリン、n-ドデカンなどの有機液体及び油、水、エタノール水溶液が上質紙、塗工紙に吸収される速度をブリストー法によって測定したところ、次の結論が得られた。
１．有機液体ではLucas-Washuburnの式に従い、Ｖ-√γt／η図では、どの液体もほぼ同一直線上にプロットされることが分かった。しかし、各有機液体の持つ官能基の違いによってセルロースを膨潤させる程度が異なり、微妙な変化が生じると考えられる。
２．エタノール水溶液を吸収させると、初期の濡れ時間と考えられている液体転移の起こらないはずの時間でも液体転移量が漸増することが観察され、その増加の割合はエタノール濃度の増加にしたがって大きくなっている。弱サイズ上質紙に対する水、エタノール水溶液の吸収でも接触時間に比例した液体の吸収が観察され、Bristow の提唱した式は適用できない。この原因として膨潤や蒸気層からの水の吸着の影響が考えられる。
３．ブリストー法から求められる表面粗さ指数を有機液体の吸収直線から算出した結果、未塗工紙のワイヤー面、フェルト面の平滑性の差はベック平滑度に対応するが、塗工紙との比較は、表面の化学的性質、圧縮性の相違により不可能であると考えられる。